Product introduction
|
● Two-component acrylics adhesive
● It is applicable to metal, alkene, PU and other materials
● It has low chromaticity, strong adhesive force and certain stress resistance
● Y-1210 is highly transparent product. It is especially applicable to products with demand in transparency
|
Physical characteristics
|
Model
|
Y-1200
|
Y-1210
|
Y-1220
|
Appearance
|
Faint yellow transparent thick liquid
|
Colorless and transparent thick liquid
|
Faint yellow transparent thick liquid
|
Solid ingredient(%)
|
42.0±1.0
|
36.0±1.0
|
47.0±1.0
|
Viscosity(cP/25℃)
|
10000-16000
|
8000-18000
|
6000-12000
|
Solvent
|
Toluene·Ethyl Acetate
|
|
Mechanical property
|
Model
|
Y-1200
|
Y-1210
|
Y-1220
|
Curing agent
|
Y-101+T0
=0.56%+0.56%
|
Y-101+T0
=0.56%+0.56%
|
Y-101+T0
=0.9%+0.9%
|
Adhesive force(gf/25mm)
|
1000-1400
|
800-1200
|
1000-1400
|
Retentivity(mm)
|
0-0.8
|
0-0.5
|
0-0.7
|
Initial adhesive force
(steel ball No.)
|
5-15
|
15-25
|
6-14
|
Maturation condition
|
23℃×7day or 40℃×24H
|
Packaging specification
|
180kg/ barrel (iron)
|
170kg/ barrel (iron)
|
180kg/ barrel (iron)
|
|
Test methods
|
1.Test material SUS304, testing environment 23℃/65%RH
2.Structure: 25μm PET+25μm dry PSA
3.Adhesive power: 180° stripping (300mm/min) after 20min
4.Retentivity: Fitting area 20mm×20mm, load 1Kg, 40℃×1h. Read the falling distance of rubber surface
5.Initial adhesive force: Testing result of J.Dow Law is the steel ball number
|
Application method
|
The adhesive is applicable to single or double-sided pressure-sensitive adhesive, such as nonwovens, foam and double-sided PET tape in household appliances and automobile industry.
Mix treatment: Take the same weight of Y - 101 and TO, stir sufficiently, then slowly add to adhesive in stirring condition, and continue stirring for 20 minutes
Drying condition: 80-100℃,1-2min(25μm dry)
|
Storage
|
Storage condition: 5-30℃ shady and cool place with good ventilation conditions
Storage period: Half a year
|
|
|
Data involved in the abovementioned product information is within the specification range of actual testing value after modification.
|
|
|